If it had been welded correctly then the weakest area is the "Heat Affected Zone" or HAZ. A failure in the HAZ would be next to the weld not through the middle of the weld. Something was not set up correctly or poor penetration, IMO.
Note, simply re-welding would likely result in the same failure, not worth the risk IMO.
Lee
|